緯綁扎帶
詳細說明：環氧樹脂浸漬玻璃纖維網狀無緯綁扎帶（符合滬Q/JBQR18-2001）
Epoxy Resin Treated Fiberglass Web Unindirectional Banding Tape （In According With Shanghai Q/JBQR18-2001） 具有網狀結構的電工用網狀無緯帶是電機和變壓器行業理想的緊固綁扎材料，不僅具有優良的柔軟性和粘性，儲存期達一年（5℃），而且拉開呈網狀結構（拉開寬度為原帶寬2倍以上），不散絲，無疊痕，退卷容易等特點。其優良性能還在于具有高抗張，高抗沖擊，高模量、低延伸、無磁滯和無渦流等特點。
本產品不僅適用于普通電機轉子、變壓器芯子的緊固綁扎，還可以用于大型特種電機的綁扎，zui大綁扎力可達100N/mm。
Epoxy Resin Treated Fiberglass Banding Tape With Web Structure is an ideal banding material for applying to the electrical machines.This banding tape is not only pliable and slightly tacky but also can be unwinded freely from the spool with out glass strands separation and overlapping.When it is pulled open the web structure will appear and the width of the tape may be extended to over twice the swize of the original.It also can be storaged for one year at the temperature of 5℃.In addition,this product possesses its desitinctive characteristics of high tensile strength,high resistance to shock,high modulus of elasticity and low percent elongation at break as well as no magnetically-confining and eddy losses.
Banding armatures of rotating electrical machines or blocking transformer colums is not the only use of this tape,and also applicable to the large-scale and special type electrical machines ect.Its max pull,When banding,can reach 100N/mm.
| 型號Type | 環氧型Epoxyglass |
| 厚度Thickness（mm） | 0.30±0.03；0.20±0.02；0.17±0.02 |
| 寬度Width（mm） | 10±0.5；15±0.5；20±1.0；25±1.0 |
| 長度Length（mm） | 150±10；200±10 |
其它規格可協商Other type required can be supplied through negotiation.
| 主要技術性能Characteristics: |
| 揮發份 | Volatile content by weight | <5% | |||||
| 含膠量 | Resin content | 27±2% | |||||
| 可溶性樹脂含量 | Solubility resin content | ≥90% | |||||
| 抗拉強度 | Teneile strength | 常態 Room temperture | ≥900MPa | ||||
| 熱態 at 150℃ | ≥560MPa | ||||||
| 絕緣等級 | Thermal Class |
| F | ||||
| 儲存期 | Storage life | 儲存溫度 Storage temperture℃ | 5 | 10 | 15 | 20 | 25 |
| 儲存時間（月）Storage time | 12 | 8 | 6 | 4 | 3 | ||
| 固化條件 | Curing conditions | 溫度 temperture℃ | 155 | ||||
| 時間（小時）Time（hours） | 6～10 | ||||||
| 產品使用率 | Utilization ratio | ||||||